RAL 2001 Red orange polyester powder , high temperature powder coating for instruments
Powder Coating is the application of organic powder by electrostatic attraction to metal, iron, copper, stainless steel. Once cured by heat the finish is a smooth, hard skin. All processes are factory applied under controlled, stable conditions. This provides significant benefits over traditional wet painting.
More textures be choiced too.
The products include high light ( above 86%),
super matt (below 20%).
We also offer a variety of shiny products according to the needs of users.
|pplication Field||Apply to anticorrosive and insulative products:|
|Anticorrosion pipeline,rebar,bridge,steel structure,|
|pylon,tank,marine fittings,electric control cabinet,|
|switch components,lighting sets.|
|Application Condition||Electrostatic spray/Triboelectric gun spray.|
|Recommended curing condition:200 degree centigrade for 12 minutes|
|(object surface temperature),range from 190 degree centigrade|
|for 20 minutes to 210 degree centigrade for 8minutes.|
|Recommended film thickness:50~80um, range from 40~150um|
|Physical Property||Specific gravity||1.4~1.8g/cm3 as per formula and color|
|Particle size||average 35~40um|
|Test Condition||Substrate||0.5mm thickness cold rolled steel sheet|
|Pretreatment||Remove rust and grease|
|Curing temperature||200 degree centigrade for 12 minutes|
|Mechanical Property||Pencil hardness||ISO 15184:1998,2H|
|Adhesion (by griding)||GB/T 9286-1998,0grade|
|Impact test||GB/T 1732-1993,≥50 kg.cm|
|Bending test||GB/T 6742 ,≤2mm|
|Cupping test||GB/T 9753,≥7mm|
|Chemical and Durability Test||Salt spray test||GB/T 1771,≥1000 hours,no obvious change ,|
|crossion width at cross≤2mm|
|Heat and moisture test||GB/T 1740,≥1000 hours,no change|